Bambu Lab - PC FR
Bambu PC FR is a high-performance polycarbonate engineered for demanding applications requiring superior flame retardancy, impact resistance, and heat stability. With outstanding durability, Bambu PC FR excels across a wide range of professional applications, including industrial components, protective casings, and high-temperature environments in sectors like automotive, electronics, and manufacturing.
Β
Top-Tier Flame Retardancy
Tested to meet to theΒ UL 94-2023 V-0Β standard, the top level of flame resistance for 3D printing filament, Bambu PC FR is engineered to prevent or slow flame propagation with exceptional self-extinguishing properties. Ideal for critical applications in electronics, automotive, and mechanical engineering.
Β
* UL 94 is a plastics flammability standard established by Underwriters Laboratories (USA). V-0βthe highest UL 94 V ratingβindicates that burning stops within 10 seconds on a vertically positioned specimen, with dripping particles allowed as long as they are not ignited.
Β
Engineering-Level Mechanical Properties
Bambu PC FR is an engineering-grade material with toughness comparable to PAHT-CF. Its exceptional stiffness and strength make it a top choice for structural components and protective casings.
Β
Accessory Compatibility
| Β | Recommended | Not Recommended |
| Build Plate | Smooth PEI Plate,Textured PEI Plate | Cool Plate SuperTack |
| Hotend | All Size / Material | / |
| Glue | Bambu Liquid Glue Glue Stick | / |
| AMS & AMS lite | AMS | AMS lite |
Product Features
- UL 94-2023 V-0 Flame Retardancy
- Engineering-Level Mechanical Properties
- Comes with High Temperature Reusable Spool
- Diameter: 1.75 mm +/- 0.03 mm
Cautions for Use
- AMS Compatible
- AMS liteΒ NOTΒ Compatible
- Dry Out before Use
Recommended Printing Settings
| Drying Settings (Blast Drying Oven) | 80 Β°C, 8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 260 - 280 Β°C |
| Bed Temperature (with PVP Glue) | 90 - 110 Β°C |
| Printing Speed | < 300 mm/s |
Physical Properties
| Density | 1.18 g/cmΒ³ |
| Vicat Softening Temperature | 114 Β°C |
| Heat Deflection Temperature | 113 Β°C |
| Melting Temperature | 225 Β°C |
| Melt Index | 26.4 Β± 2.7 g/10 min |
Mechanical Properties
| Tensile Strength | 60 Β± 4 MPa |
| Breaking Elongation Rate | 2.4 Β± 0.3 % |
| Bending Modulus | 1890 Β± 70 MPa |
| Bending Strength | 90 Β± 4 MPa |
| Impact Strength | 55 Β± 2.1 kJ/mΒ² |
Printing Tips
Drying ConditionsοΌ
Dry before use for higher printing quality. PC FR must be dried before use and kept moisture-free during the printing process. Store in a dry environment, such as an airtight storage container with a desiccant, after use. For more details, please refer to: Printing tips for Engineering materialsΒ on WIKI.
- In a blast drying oven: 80Β°C for 8 hours.
- On an X1 printer's heatbed: 90Β°C to 100Β°C for 12 hours.
Safety Attention:
The nozzle temperature should be between 260-280Β°C, and the heat bed temperature should be between 90-110Β°C. Please ensure safety during printing.