Bambu Lab PA6-GF
Bambu PA6-GF - Glass Fiber Reinforced Nylon
Bambu PA6-GF, also known as Nylon 6 with Glass Fiber, stands at the forefront of high-performance engineering plastics. Engineered to deliver exceptional strength, durability, dimensional stability. The PA6-GF is also more cost effective when compared to other top tier engineering filaments.
Built to Last
Bambu PA6-GF is exceptionally strong and durable due to reinforced glass fibers, making it the perfect choice for prints that need to withstand heavy use and resist bending or breaking.
Dimensional Stability
PA6-GF boasts unparalleled dimensional stability thanks to its glass fiber reinforcement, minimizing warping in comparison to standard PA filaments. Print with precise dimensions, even in the most intricate geometries.
Exceptional Thermal Properties
PA6-GF boasts a high heat deflection temperature and superior dimensional stability, enabling it to retain its mechanical properties even under elevated temperatures. This makes it ideal for demanding industrial and automotive applications.
Chemical Resistance
PA6-GF offers excellent resistance to chemicals, oils, and many kinds of solvents, ensuring long-term performance in challenging environments.
Smooth Surface and More Colors
Bambu PA6-GF filaments are compatible with the Bambu AMS system, ready to print in multi-color. The special surface texture also blurs the layer lines, providing a smooth surface quality.
Product Features
- Built to Last
- Dimensional Stability
- Exceptional Thermal Properties
- Chemical Resistance
- Smooth Surface and More Colors
- Diameter: 1.75mm +/- 0.03mm
Cautions for Use
- 0.2 mm Nozzle Not Compatible
- Stainless Steel Nozzle Not Recommended
- AMS Compatible
- AMS lite NOT Compatible
- Dry before Use
Recommended Printing Settings
| Recommended Printing Settings | |
| Drying Settings before Printing | 80 °C, 8 - 12 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 260 - 290 °C |
| Bed Temperature (with Glue) | 80 - 100 °C |
| Printing Speed | < 130 mm/s |
Physical Properties
| Physical Properties | |
| Density | 1.14 g/cm³ |
| Vicat Softening Temperature | 210 °C |
| Heat Deflection Temperature | 182 °C |
| Melting Temperature | 219 °C |
| Melt Index | 9.0 ± 0.8 g/10 min |
Mechanical Properties
| Mechanical Properties | |
| Tensile Strength | 75 ± 6 MPa |
| Breaking Elongation Rate | 3.9 ± 0.8 % |
| Bending Modulus | 3670 ± 140 MPa |
| Bending Strength | 120 ± 6 MPa |
| Impact Strength | 27.2 ± 2.2 kJ/m² |